毕业论文-----含硫原油加工过程中的硫腐蚀

《毕业论文-----含硫原油加工过程中的硫腐蚀》由会员分享，可在线阅读，更多相关《毕业论文-----含硫原油加工过程中的硫腐蚀（20页珍藏版）》请在毕设资料网上搜索。

1、含硫原油加工过程中的硫腐蚀 摘要：结合石油化工设备硫腐蚀的特点，从3个方面对炼油厂的硫腐 蚀问题进行了理论分析与简述。从硫腐蚀现状来看，已经对炼油设备 造成了严重腐蚀，而且贯穿于炼油的全过程；从机理来看，硫腐蚀类 型较多、过程比较复杂，许多机理性问题还远远没有研究清楚；从目 前实际情况看，应加强对硫腐蚀机理的研究，弄清硫腐蚀的规律，为 控制原油加工过程中的硫腐蚀提供理论基础。 关键词：高硫原油 设备 控制 腐蚀 Abstract: combining petrochemical equipment characteristics of sulfur corrosion, from three

2、aspects of the refinery sulfur corrosion problems were analyzed in theory and briefly reviewed. Judging from sulfur corrosion situation of refining equipment, has caused a serious corrosion, and throughout the whole process of refining; Judging from mechanism, sulfur corrosion type more, process mor

3、e complicated, many machine rational problem is far from research clear; From the actual situation look, should strengthen the research of the corrosion mechanism of sulfur, make clear the pattern of sulfur corrosion control processing crude oil provides the theoretical foundation of sulphur corrosi

4、on. Keywords: sour crude equipment control corrosion 目录 第1章概述 第2章原油中的硫和硫化物 21含硫化合物的存在形态及分布 22活性硫 23含硫原油炼制过程中活性硫的由来和形成 第3章活性硫腐蚀的主要过程和腐蚀机理 31活性硫腐蚀的主要过程 3.2进口原油腐蚀性介质调查情况 第4章国内加工含硫原油的防腐蚀工作 41规范防腐蚀管理 42材料表面技术改性开发 43 防腐蚀技术的创新 44今后应开展的工作 第5章 加工含硫原油设备存在的隐患 5.1常顶空冷器泄漏 5.2减压渣油换热器发生自燃 5.3焊缝发生开裂泄漏 5.4膨胀节开裂 5.5空冷器出口法兰焊缝开裂 5.6法兰密封垫圈开裂 5.7加氢精制汽提塔顶回流罐内壁裂纹 5.8螺栓断裂事故常有发生 5.9球罐出现微裂纹 5.10烟气露点腐蚀 5.11油罐腐蚀 5.12自燃 第6章常规的防腐蚀措施 61 工艺防护 62材质升级 63实时在线监测 64防腐结构优化设计 第7章 国内外对加工高硫原油腐蚀控制情况 71 强化工艺防腐蚀技术 72合理选材 7